Özgün Başlık Deposition, Structural and Optical Properties of the Cdznsse Films Yazarlar Yasemin Çağlar, Muhsin Zor Dergi Adı Eskişehir Teknik Üniversitesi Bilim ve Teknoloji Dergisi A - Uygulamalı Bilimler ve Mühendislik - ESTUJST-A Cilt 2003, Cilt 4, Sayı 1, ss. 53-58 Anahtar Kelimeler Compound Semiconductors ; Spray Pyrolysis ; X-Ray Diffraction ; Energy Band Gap Özet CdZnSSe films have been produced by the spray pyrolysis method on to the glass substrates kept at various substrate temperatures and with varying Se contents. The X-rays diffraction spectra of the films have shown that the films produced are polycrystalline and hexagonal in structure. The films have exhibited direct band gap characteristics with the band gap values lying in the range between 2.82-2.97eV. Başlık (Yabancı Dil) Cdznsse Filmlerinin Elde Edilmesi, Yapısal ve Optiksel Özellikleri Anahtar Kelimeler (Yabancı Dil) Bileşik Yarıiletkenler ; Püskürtme ; X-Işını Kırınımı ; Yasak Enerji Aralığı Özet (Yabancı Dil) CdZnSSe filmleri püskürtme yöntemi ile cam tabanlar üzerine farklı Se miktarları ve farklı taban sıcaklıklarında elde edilmişlerdir. X-ışını kırınım desenleri filmlerin hekzagonal ve polikristal yapıda olduklarını göstermektedir. Filmlerin yasak enerji aralığının direkt bant geçişli olduğu ve değerlerinin 2, 82-2, 97eV arasında değiştiği belirlenmiştir. |